| 产品特性：耐火温度高 | 是否进口：否 | 产地：HENAN |
| 品牌：四成研磨 | 型号：40-70 | 种类：铬铁矿砂 |
| 规格：一级 | 材质：铬铁矿 | 粒度：40-70目 |
| 适用范围：钢铁铸造 | CR2O3含量：46% | 烧结温度：1800吨 |
| 原产地：南非 | 比重：4.2-4.8g/cm3 | 堆积密度：2-2.2g/cm3 |
| 硅含量：低于1% |
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm广泛用于熔模铸造、自硬砂铸造、消失模铸造等。铸造用的铬铁矿砂来自南非优质矿山。 南非铬矿的Cr2O3纯度不低于46%。 与耐火级铬铁矿砂相比，铸造铬铁矿砂应具有较高的Cr2O3含量和均匀的颗粒分布。铸造级铬矿砂适用于大型铸钢件、厚壁铸件、局部厚壁铸件，中小型铸件铸造用面砂，可以代替硅砂，提高铸件的表面光滑度，降低次品率。对一些小型铸件，可代替锆英砂，达到节省成本又不太影响铸件质量的目的。
Chrome ore sand 0.2-0.4mmis widely used in investment casting, no-baked sand casting, lost foam casting,etc. The best chromite sand for foundry is from good quality mine in South Africa. The Cr2O3 purity of SA chrome ore is min 46%. Comparing with refractory grade chromite sand, the foundry chromite sand should be high Cr2O3 content and with good particle distribution. Foundry chromite sand will help foundries to get a smooth finish surface of steel castings.
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm的物理指标：
莫氏硬度 | Mohs:5.5-6 |
熔点 | Sublimes at 2180 ℃ |
烧结温度 | ＞1800℃ |
比重 | 4.0-4.8 g/cm3 |
堆积密度 (LPD): | 2.5-3 g/cm3 |
颜色 | Black |
PH值 | 7-9 |
游离酸含量 | 0% |
酸度 | ≤2ML |
浑浊度(JTU) | 110 |
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm的化学成分：
Cr2O3 | ≥46.0% |
SiO2 | ≤1.0% |
FeO | ≤26.5% |
CaO | ≤0.3% |
MgO | ≤10% |
AL2O3 | ≤15.5% |
P | ≤0.003% |
S | ≤0.003% |
Cr/Fe | 1.55:1 |
土质含量 | ≤0.1 |
水分含量 | ≤0.1 |
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm的性能特点：
1、耐碱性渣好，不与氧化铁反应。
在实际应用中，铬矿砂可以避免热化学砂粘在铸件表面。因而减少了铸造中出现的“重皮”、“橙皮”等表面缺陷，进而节省后道工序表面处理的投入。
2、铬铁矿砂是一种惰性铸造砂，对钢水的润湿角大。这使得对钢液具有良好的抗润湿性。铬铁矿砂不会与钢水发生反应。在熔模铸造过程中，铬矿本身经过固相烧结，防止了熔融金属的渗透，不会产生化学粘砂。
3. 导热性和蓄热系数比硅砂高好几倍。铬铁矿砂的这种特性可以提高熔化钢液的冷却速度。一方面，它防止在高温下发生化学反应，因此铸造会从外壳上脱落，更容易清洁铸件表面。
另一方面，它也增加了钢水的凝固过程。它会使铸钢件的缩孔和气孔更少。
4. 耐火度高。耐高温性将有助于在钢水进行浇筑时保持型砂的化学稳定性。
5. 热膨胀系数低。铸造铬铁矿砂的这种特性将有助于增加铸件上的不成形缺陷。
6. 颗粒筛分布均匀。铬铁矿砂粒度严格按照AFS标准获得。通过多重清洗工艺，我们生产的铬铁矿砂浊度低。这将使铬铁矿质量的一致性。
7. SiO2 含量低于1%。这将有助于防止铸件上出现重皮粘砂缺陷。
Product Feature and Applications of Chrome ore sand 40-70#:
1. Good resistance to alkaline slag and does not react with iron oxide.
In practical applications, chrome ore can avoid thermal chemical sand sticking on surface of casting. Thus it will save cost on further surface finish work.
2. High Wetting angle to molten steel liquid.
That makes good wetability resistance to steel liquid. Chromite sand won’t get react with molten steel. There won’t be chemical sand sticking for casting steels.
3. High thermal conductivity and thermal storage coefficient
It is several times greater than that of silica sand. That property of chromite sand can
increase the cooling speed of melted steel liquid. On one hand, it prevent chemical reaction in high temperature. So casting will get off from the shell. It is easier to clean the casting surface.
On the other hand, it also increase the solidification process of molten steel. It will make less shrinkage and porosity of steel castings.
4. High refractoriness
The resistance to high temperature will help chromite sand stable to molten steel.
5. Low thermal expansion.
That property of foundry chromite sand will help to decrease the unshaped defects on castings.
6. Even particle sieve distribution. The chromite sand grit size is get strictly according to AFS standard. By multi cleaning process, the chromite sand from us is with low turbidity. That will make the consistency of chromite quality.
7. Low SiO2 content. It will help to prevent heavy leather defects on castings.
锰铬钢铸造用天然铬矿砂AFS40-45Chrome ore sand 0.2-0.4mm的应用范围：
熔模铸造。用于精密铸造的外壳成型，如水玻璃外壳成型。
碳钢和高锰钢铸造用造型砂和制芯的混合材料。
可以作为钢包的浇筑添加材料，钢包水口引流砂的添加材料。
水玻璃结合剂的自硬砂工艺，用于碳钢或铬锰钢的铸造。
消失模铸造和覆膜砂铸造。
适合大型铸件或特大型铸件的湿型砂。
精密铸造中，可以作为制壳面砂（铬铁矿砂）和铸造涂料（铬铁矿粉）使用。?
低硅高铬造型砂的型号：
国内常规粒度：10-20#，20-40#，20-60#，30-70#，40-70#，50-100#、70-140#，140-270#， 0-1mm， 200#，325#,400#，70#-0
出口常规粒度：AFS25-35 AFS25-30 AFS30-35 AFS35-40 AFS40-45 AFS45-50 AFS40-50 AFS50-55 AFS55-60 AFS60-65 0-1mm 200# 325#,400#